1
9415
MVR (300 °C/1.2 kg) 6.0 cm3/10 min; 10 % glass fiber reinforced; flame
retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; easy release; injection molding – melt temperature 310 – 330 °C; available in opaque colors only
2
9417
MVR (300 °C/1.2 kg) 6.0 cm3/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; UV-stabilized; easy release;
injection molding – melt temperature 310 – 330 °C; available in opaque colors only
3
GF9002
MVR (300 °C/1.2 kg) 15 cm3/10 min; 10 % glass fiber reinforced; flame
retardant UL 94V-0/1.2 mm; low viscosity; easy release; injection molding – melt temperature 310 – 330 °C; available in opaque colors only; electrical/electronic; housing parts with low wall thickness
4
GF8001
MVR (300 °C/1.2 kg) 16 cm3/10 min; 20 % glass fiber reinforced; low viscosity; easy release; injection molding – melt temperature 310 – 330 °C; available in opaque colors only; housing parts
5
9125
MVR (300 °C/1.2 kg) 8.0 cm3/10 min; 20 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm; medium viscosity; easy release; injection molding – melt temperature 310 – 330 °C; available in opaque colors only
6
8325
MVR (300 °C/1.2 kg) 4.0 cm3/10 min; 20 % glass fiber reinforced; high viscosity; easy release; injection molding – melt temperature 310 – 330 °C; extrusion; available in opaque colors only
7
9425
MVR (300 °C/1.2 kg) 5.0 cm3/10 min; 20 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; easy release; injection molding – melt temperature 310 – 330 °C; extrusion; available in opaque colors only
8
8345
MVR (300 °C/1.2 kg) 3.0 cm3/10 min; 35 % glass fiber reinforced;
high viscosity; easy release; injection molding – melt temperature 310 – 330 °C; extrusion; available in opaque colors only